In this study, XRF, loss in ignition, SEM, and PSA analysis were performed on four types of fly ash in Vietnam and compared with fly ash in Korea. As a result, it was found that PC boiler fly ash in vietnam has a similar chemical composition in which the content of SiO2, Al2O3, and Fe2O3 accounts for about 70% from the one korea fly sah. In addition, the result showed that the national quality standards and its performance of blast furnace slag in Vietnam were similar with the ones in Korea. A binder material mixing test using four types of fly ash supplied from Vietnam was conducted, and the compressive strength in the range of 7.60∼13.25 MPa was measured as of 28 days of curing. Vinh Tan fly ash raw material showing the highst compressive strength was selected and used as the soil injection material of the chemical grouting method. For the formulation of the chemical grouting method, sodium silicate No.3 and silica-sol were used as liquid-A. As a result of measuring the gel time and the compressive strength of homogel, they showed good performance satisfying the standards applied in Korean construction fields. Therefore, Vinh Tan fly ash can be used as a soil injection material for the chemical grouting method.
본 연구에서는 베트남에서 발생하는 4종의 플라이애시에 대하여, XRF, 강열감량, SEM, PSA분석을 실시하였고, 국내 발생 화력발전 플라이애시와 비교하였다. 그 결과 PC보일러 플라이애시의 경우, SiO2, Al2O3, Fe2O3의 함량이 약 70 %를 차지하여 국내플라이애시와 비슷한 화학조성을 갖는 것으로 나타났다. 또한, 베트남 고로슬래그와 국내 고로슬래그를 비교한 결과 유사한품질기준과 성능을 나타내는 것으로 확인되었다. 베트남에서 수급한 4종의 플라이애시를 이용하여 지반주입재 배합시험을 실시하였으며, 양생 28일 기준 압축강도는 7.60∼13.25 MPa로 나타났다. 가장 압축강도가 크게 나타난 Vinh Tan 플라이애시 원료를선정하여 약액주입공법용 지반주입재 원료로 활용하였다. 약액주입공법의 배합은 급결재로서 규산소다 3호와 실리카졸을 사용하였다. Vinh Tan 플라이애시를 사용한 지반주입재의 겔타임과 호모겔 압축강도를 측정한 결과 국내 건설현장 적용기준을만족하는 것으로 나타나, Vinh Tan 플라이애시의 경우 약액주입공법용 지반주입재로 활용이 가능할 것으로 사료되었다.