A detailed experimental investigation was performed at a single maximum cyclic stress (sigma max) level to physically characterize the progression of thermomechanical fatigue (lW) damage in continuously reinforced (0 deg) SCS-6/Timetal 21S, a titanium matrix composite. In-phase (IP) and out of-phase (OP) loadings were investigated at sigma max = 1000 MPa with a temperature cycle from 150 to 6500 C. Damage progression, in terms of macroscopic property degradation, was experimentally quantified through an advanced TMF test methodology which incorporates explicit measurements of the isothermal static moduli at the TMF temperature extremes and the coefficient of thermal expansion (CTE) as functions of the TMF cycles. Detailed characterization of the physical damage progression at the microstructural level was performed by interrupting multiple TMF tests at various stages of mechanical property degradation and analyzing the microstructure through extensive destructive metallography. Further, the extent of damage was also quantified through residual static strength measurements. Results indicated that damage initiation occurred very early in cyclic life (N less than 0.1Nf) for both the IP and OP TMF loadings. IP TMF damage was found to be dominated by fiber breakage with a physical damage progression in the microstructure which was difficult to quantify. OP TMF loadings produced matrix cracking exclusively associated with surface initiations. Here, damage progression was easily distinguished in terms of both the number of cracks and their relative inward progressions toward the outer fiber rows with increased cycling. The point at which the leading cracks reached the outer fiber rows (when localized fiber/matrix de-bonding and matrix crack bridging occurred) appeared to be reflected in the macroscopic property degradation curves.