The present work shows the fractal analysis for the microstructure of Al-6Si-3Cu-xMg (x = 0.59, 3.80 and 6.78 wt.%) alloys, solution heat treated at 480 °C for times ranging from 4 to 72 h. Microstructural changes were examined using Optical Microscopy (OM) and Scanning Electron Microscopy (SEM), and quantified by measuring conventional characteristics of second phases. The fractal analysis of the microstructures was also carried out using fractal dimension (Df). Results shown important variations in the microstructure when Mg content is increased, being the eutectic Al-Si and Cu-rich phases the predominant phases for the alloys with low Mg content, while for higher Mg contents predominant phases were Mg2Si and Cu-rich phases. The analysis of Df showed that this parameter could be used in order to compare the microstructural solution response of the Al alloys. Besides, it was possible to correlate the fractal dimension with the shape factor of the second phases, mainly for the alloys with only one second phase remaining after heat treatment.