When manufacturing concrete, several mineral admixture is added to improve the basic physical property and durability and to make economical concrete. Such mineral admixture includes granulated blast furnace slag, fly ash, silica fume, etc., and not only the studies about mixing these mineral admixtures but also the studies for the development of new materials have been steadily in progress. The purpose of this study was to investigate the development of concrete durability using rice straw ash. It is used for chloride diffusion coefficient from rapid chloride penetration test and depth of Co2 penetration from rapid carbonation test that was used for the evaluation of latent durability. According to the experimentation result, when replacement ratio of rice straw ash e was increased from 0% to 10%, it was observed that compressive strength of concrete containing rice straw ash was a similar durability of concrete containing silica fume. And durability performance of concrete containing rice straw ash 10% show a excellent compared to concretes containing granulated blast furnace slag 30 % or fly ash 20 %.
콘크리트를 제조하는데 있어, 경제적이면서 내구성과 물리적 특성을 향상시키기 위해 광물성 혼화재가 사용되고 있다. 일반적으로 사용되고 있는 광물성 혼화재로서는 대표적으로 플라이 애쉬, 고로슬래그 미분말 그리고 실리카 흄 등이 있으나 새로운 재료의 개발이 시급하다. 본 연구에서는 소성볏짚을 혼입한 콘크리트의 압축강도, 염화물 확산계수 및 촉진중성화 시험을 통하여 기존의 광물성 혼화재료를 혼입한 콘크리트와 비교, 분석함으로써 소성볏짚의 혼입에 따른 내구성능 향상을 알아보았다. 실험결과에 따르면, 소성볏짚을 0에서 10%까지 혼입하였을 때 실리카흄을 혼입한 경우 시편과 유사한 내구성능을 보였다. 그리고 촉진중성화 및 염화물확산 시험결과에서도 소성볏짚을 10 % 혼입한 콘크리트 시편에서 고로슬래그 미분말 30 % 또는 플라이 애쉬 20 %를 혼입한 시편과 비교하여 내구성능이 우수한 것으로 나타났다.