A sodium salt of a modified lignosulfonate at different percentages was added to a porcelain stoneware suspension and the effects on the rheological properties of slips and on the mechanical properties of prepared samples were investigated. As the presence of sulfonates groups can change the stability of dispersion, a rheological characterisation was necessary to find the critical concentration to obtain well dispersed suspensions and high MOR values. The suspensions stability was tested by oscillatory measurements and the increase of elastic modulus in the suspension corresponded to a MOR and to Young’s modulus increase as well. Finally, to explain the results obtained by the mechanical characterisation of the prepared samples, a model drawing on the composite materials experience, is suggested.Usando distintos porcentajes, se añadió sal de sodio de un lignosulfonato modificado, a una suspensión de gres porcelánico, y se investigaron los efectos sobre las propiedades reológicas de las suspensiones y sobre las propiedades mecánicas de las muestras preparadas. Debido a que la presencia de grupos de sulfonatos puede modificar la estabilidad de la dispersión, fue necesario realizar una caracterización reológica para averiguar la concentración crítica necesaria para la obtención de suspensiones bien dispersas y altos valores de MOR. Se analizó la estabilidad de las suspensiones por medio de mediciones oscilatorias y el incremento del módulo elástico en la suspensión que corresponde al incremento de un módulo MOR y de un módulo de Young también. Finalmente, para explicar los resultados obtenidos por medio de la caracterización mecánica de las muestras preparadas, se sugiere un modelo que parte de la experiencia con los materiales compuestos.